Epoxy zinc-rich primer 
 Overview: from epoxy resin, polyamide resin, ultra-fine zinc powder, solvents, additives and other components of the two-component coating with cathodic protection and shielding effect, anti-rust performance, room temperature drying, strong adhesion, oil, water - SUI good, with a variety of supporting the use of anti-corrosion coating. 
 Application: suitable for marine engineering, ship, tank, gas tank, tank piping, bridges, towers, oil pipelines and other facilities, heavy-duty steel surface. Is the epoxy intermediate coat and finish the best epoxy primer. 
 Technical parameters 
 Item Index 
 Exterior paint color and gray, smooth 
 Drying time (25 ± 1 ℃), h is dry ≤ 1, ≤ 24 hard work 
 Adhesion level 2 
 Flexibility mm 2 
 Impact resistance kg.cm 50 

 Construction Parameters 
 Ratio ratio (mass ratio to a barrel labeled date): A: B = 10:1 
 Coating thickness 40-60μm / Road 
 Theoretical amount of 200-250 g / m 2 (without loss) 
 Spray coating method, brush, roller coating 
 Surface rust has reached the standard Sa2.5 level, so that the surface dry and flat. 
 Painting Road, Road Number 1-2 
 , After supporting the FY-86-2A epoxy intermediate coat of iron 
 Storage period of 12 months 

 Notes 
 Steel surface to be sand-blasting, to GB8923 "steel surfaces before painting Rust grades and preparation," the provisions of the Sa2.5 grade level. Stir after the opening of paints to be, I provided the ratio A, B two copies, with a good 30 minutes after brushing ripening. Is best used within two hours. If you are experiencing low temperature, coating time interval should be extended, outdoor construction, to avoid rain, fog, snow, after a good paint brush, paint brush into temporarily, direct vision should not exceed 7 days. 
 This product is valid for 12 months.