Corrosion with aluminum foil UV / pipe anti-corrosion weathering tape | aluminum corrosion tape | tape wrapped around the cold 
 First, product technology and use: 
 Corrosion with aluminum foil, and some manufacturers also known as: PipeCoat corrosion aluminum foil tape, adhesive type is a high UV resistance and strong anti-foreign anti-corrosion protection of new materials. This product is primary for the toughening of aluminum foil sheet, with butyl rubber modified asphalt layer, a layer of isolated anti-sticking film and salty. 
 This product is mainly used for natural gas, petroleum, chemical, pharmaceutical, heat, urban construction in the oil, gas, water, heating pipe or tower overhead corrosion protection structure. As a result of the unique products reflecting strong sunlight and UV resistance and flexibility, smooth appearance of the aluminum foil substrate and a high corrosion resistance, strong bond of the butyl rubber modified asphalt adhesive is made. Solid and the aluminum foil tape with a waterproof anti-corrosion, aging, not curing, not cracking, long-term move does not appear, do not peel and other fine features, so as to achieve the anti-corrosion ability, the effect of beautiful appearance, the product is proven by the excellent The U.S. anti-corrosion share. Executive Standard SY / T 0414-2007. 
 Item Unit Parameter 
 Color Appearance / white flash 
 Kimo thickness mm 0.50 
 Layer thickness mm 0.50-1.00 
 Total thickness mm 0.10-1.50 
 Tensile strength Mpa ≥ 100 
 Elongation at break% 800 
 Shear performance (on the back material) N/25mm ≥ 50 or the bonding surface 
 (For aluminum) outside the fault 
 Stripping Performance N/25mm ≥ 40 
 Low temperature flexibility (-10 ℃, 20mm, 3s, 180o) no cracks 
 Heat resistance (120 ℃) ??without sliding 
 Dielectric strength Mv / m ≥ 25 
 Volume resistivity Ω.M 2 × 1010 
 Water Vapor Transmission Rate (24h) Mg/cm2 く 0.45 
 Water absorption% ≤ 0.35 
 Resistant to temperature ℃ -34 --- +110 


 Third, use: 
 (1), surface treatment: rust, in addition to welding slag, burrs, oil, dirt and kept clean and dry by hand should reach St3 grade rust, rust should reach Sa2 mechanical level, and meet SYJ4007 86 requirements. 
 (2), primer: primer should be dedicated support, when used away from the fire, mix well and with a clean brush, roller or other mechanical method of uniform coating, the primer amount: manual coating 12 / L Mechanical coating 20 / L,, 
 (3), to be 5-10 minutes after the primer is dry you can wound. 
 (4), the use of a temperature of -5 ℃ +50 ~ C, 
 Fourth, transportation, storage: 
 (1), anti-exposure, anti-rain, frost insulation, to prevent the crush deformation, heat and open flame near prohibited. 
 (2), transportation or storage, one at -20 ℃ +35 ℃ environment. 
 (3), save 6 months. Specific landing